SAE 1026 Mechanical Tubing ASTM A519

SAE 1026 Mechanical Tubing ASTM A519

Process Method:

Hot rolled, Cold Drawn, Cold Rolled, Honed, SRB.

Dimensions and Tolerances:

Outer diameter: 21 to 720 mm, wall thickness: 2 to 200 mm, length: Not more than 12 m.

SAE 1026 Chemical Composition (WT %)

Standard	Grade	C	Mn	P	S
ASTM A519	1026	0.22-0.28	0.60-090	0.040 max	0.040 max

Delivery Condition:

Hot Rolled, Cold Drawn, Stress Relieved, Annealed, Normalized.

Package:

All pipes shall be marked, coated with oil and capped with plastic end protector. All items shall be plain end.

Our Services:

Third Party inspection acceptable. such as SGS, BV etc.

Supplying financial support with usance L/C 180 days after B/L date.

Contact Us:

Shanghai Unite Steel

Phone: 86-15121067826

Skype: samsonhuang22

Email: samsonhuang@shunitesteel.com

Tel: 86-21-35316960   Fax: 86-21-35316961

Add: Room 1109, No. 275-8 Guoding East Road, Shanghai 200433, China

Web: www.shunitesteel.com

Tag: sae 1026 chemical composition; sae 1026 mechanical properties; sae 1026 tubing; sae 1026 steel equivalent;, 1026, sae1026 tube; astm a519, astm a519 1026, sae 1026 pipe, AISI 1026

ISO 9001：2008

E470 / 20MnV6 Steel Pipe for Hydraulic Cylinders

E470 / 20MnV6 Steel Pipe for Hydraulic Cylinders

Process Method:

Hot Rolled, Cold Drawn, Cold Rolled, Honed, SRB.

Delivery Condition:

Hot Finished(+AR), Normolized(+N), Quenched and tempered(Q+T), etc.

Dimensions and Tolerances: 

Outer diameter: 21 to 720 mm, wall thickness: 2 to 200 mm, length: Not more than 12 m.

Related Specifications:

Steel Standard	Steel Name	Steel Number
EN 10294-1 / EN 10297	20MnV6 /E470	1.0536

Chemical Composition (wt %) 

Carbon	Silicon	Manganese	Vanadium	Phosphorus	Sulphur	Aluminium	Niobium	Titanium
0.16/0.22	0.10/0.50	1.30 / 1.70	0.08 / 0.15	≤ 0.030	≤ 0.035	≤ 0.010	≤ 0.070	≤ 0.020

20MnV6 Machinability: 

Excellent machinability with high cutting speeds or improved tool life 

Heat Treatment: 

Will through harden with a moderate increase in strength and will also carburise, carbonitride or nitride.

Mechanical Properties - (Minimum at room temperature) 

Steel Name	Wall Thickness	Rp 0.2 (MPa)	Rm (MPa)	A %
20MnV6 / E470	≤ 16mm	470	650	17
20MnV6 / E470	>16mm ≤ 40mm	430	600	17

Typical (minimum) mechanical properties – Quenched and tempered 

Steel Name	WT	Yield Strength MPa	Tensile Strength MPa	Elong %	Charpy J	Hardness HB
20MnV6 / E470	≤ 16	590	700	16	40	205
20MnV6 / E470	≤ 25	540	570	16	40	160
20MnV6 / E470	≤ 50	480	570	16	-	160

20MnV6/E470 Welding: 

Excellent weldability hot rolled or cold drawn but avoid when through hardened or surface hardened. Welding details for guidance only 

  

Heat Treatment:

Normalising: Heat to 880°C Cool in still air 

Stress Relieving: Heat to 600 – 620°C Cool in still air 

Hardening: Heat to 880°C Quench in oil or water 

Tempering: Heat to 500 – 600°C (or as required) Cool in still air.

Contact Us:

Shanghai Unite Steel

Phone: 86-15121067826

Skype: samsonhuang22

Email: samsonhuang@shunitesteel.com

Tel: 86-21-35316960   Fax: 86-21-35316961

Add: Room 1109, No. 275-8 Guoding East Road, Shanghai 200433, China

Web: www.shunitesteel.com

ISO 9001: 2008

Tubo afinados St 52 / E355 por cilindro hidráulico e pneumatic

Tubo afinados St 52 / E355 por cilindro hidráulico e pneumatic

Descrição do produto

Aplicável a pressão hidráulica, cilindro pneumático, o barril de bomba de óleo, corpo do motor, eixo de transmissão, etc.

padrão de Qualidade

DIN 2391, EN 10305-1, SAE J524, ASTM A519 e GB3639.

processo

Materiais primas - drawn/rolled Fria - tratamento térmico (BKS) - afinados ou SRB- embalagem.

Tipo de aço

ST52, ST52.3, E355, SAE 1026, Q345B.

* Teste de impacto a baixa temperatura mediante pedido (27J/-40 ° C).

Tamanho

processamento	diâmetro do cilindro	Length /mm	Retidão	precisão Tamanho	A espessura da parede / mm	Rugosidade furo interno
Trefilados / Laminados	ID28~OD400	≤12M	0.3~1.0m m/m	H8-H11	±5%	0.8~1.6um
afinados / SRB	ID30~OD500	≤12M	0.3~1.0m  m/m	H8	±5%	0.4~0.8um

Tubo afinados St 52 / E355 Propriedades Mecânicas

Entrega Condição	Acabadas a frio (BK)		Estresse aliviado (BKS)
	Rm	alongamento	Rm	ReH	alongamento
	MPA	%	MPA	MPA	%
ST52	≥640	≥5	600	520	14

Embalagem e Expedição

Com óleo anti-ferrugem no diâmetro interno de cada tubo, tampas de tubos em ambas as extremidades, pacotes hexagonais de 3,000 kg com várias tiras de aço, saco de nylon e embalagem de papel impermeável cada pacote. Claro, os clientes podem personalizar outra forma de embalagem.

 Nossos Serviços

Terceiro inspeção aceitável Parte. como SGS, BV etc

Fornecimento de apoio financeiro com usance L / C 180 dias após a data de B / L.

Informações sobre a empresa

Sansão Huang

Telefone: 86-15121067826

Skype: samsonhuang22

Email: samsonhuang@shunitesteel.com

Shanghai Unite Steel

Tel: 86-21-35316960 Fax: 86-21-35316961

Adicionar: Room 1109, n º 275-8 Guoding East Road, Shanghai 200433, China

Web: www.sunitesteel.com